ESPREE™ ZYYST
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ESPREE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a4zmiz_ESPREE-ZYYST.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ESPREE™ZYYST is a polyamide 66 (nylon 66) product,. It can be processed by injection molding and is available in North America. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.5 - 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Ultimate, 3.18 mm) | 48.3 | MPa | ASTM D638 |
| Flexural Modulus 2(3.18 mm) | 1720 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 1000 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 65.6 | °C | ASTM D648 |
| Melting Temperature | 249 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.838 mm, NC | HB | UL 94 | |
| 1.65 mm, RD | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 249 - 282 | °C | |
| Middle Temperature | 260 - 288 | °C | |
| Front Temperature | 271 - 304 | °C | |
| Nozzle Temperature | 271 - 304 | °C | |
| Processing (Melt) Temp | 271 - 304 | °C | |
| Mold Temperature | 65.6 - 110 | °C | |
| Back Pressure | 0.172 - 1.03 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Complet® LGF20-TPU | PlastiComp, Inc. | ETPU | Complet® |
| Durez® 33488 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| LNP™ LUBRICOMP™ DFL32P compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| EcoHumer BFX103 | WooSung Chemical Co., Ltd. | PBAT | EcoHumer |
| Sumiliteresin® PR-16 I | SBHPP | Phenolic | Sumiliteresin® |