GLAMIDE® T-661
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a4xPvK_GLAMIDE-T-661.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GLAMIDE®T-661 is a polyamide 66 (nylon 66) product,. It is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.60 - 1.2 | -- | % | ASTM D955 |
| 3.00 mm | 1.5 - 2.2 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.2 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 2.5 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 116 | 110 | MPa | ASTM D638 |
| Yield, 23°C | 82.0 | 50.0 | MPa | ASTM D638 |
| Yield, 80°C | 38.0 | 28.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 120 | 200 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 4300 | 4000 | MPa | ASTM D790 |
| 23°C | 2900 | 1400 | MPa | ASTM D790 |
| 80°C | 1000 | 600 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 140 | 120 | MPa | ASTM D790 |
| Yield, 23°C | 117 | 66.0 | MPa | ASTM D790 |
| Yield, 80°C | 66.0 | 40.0 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 90.0 | -- | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles, CS-17 Wheel) | 8.00 | -- | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 35 | 40 | J/m | ASTM D256 |
| 23°C | 45 | 300 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 230 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 80.0 | -- | °C | ASTM D648 |
| CLTE - Flow | 8.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 20 | 13 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.90 | 6.50 | ASTM D150 | |
| Arc Resistance | 55.0 | 45.0 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Tensile Elongation, ASTM D638, 23°C: >200 %Volume Resistivity, ASTM D257: 10e10 to 10e11 ohm-mComparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 30.0 - 40.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-91-T3056S-90 | Teknor Apex Company | TPE | Telcar® |
| Fortron® 0205 | Celanese Corporation | PPS | Fortron® |
| Elastamax™ XL 0131-59(50/50) | PolyOne Corporation | SBC | Elastamax™ |
| Jamplast JPEVA18 | Jamplast, Inc. | EVA | Jamplast |
| LEXAN™ PC1800R resin | SABIC Innovative Plastics | PC | LEXAN™ |