Amilan® CM1012G-45N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a4YML4_Amilan-CM1012G-45N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Amilan® CM1012G-45N is a Polyamide 6 (Nylon 6) product filled with 45% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: heat resistant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow : 3.00 mm 1 | 0.40 to 0.60 | -- | % | |
| Flow : 3.00 mm 2 | 0.10 to 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.90 | -- | % | |
| Saturation, 23°C | 5.3 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | |||
| M-Scale, 23°C | 95 | -- | ||
| R-Scale, 23°C | 121 | -- | ||
| R-Scale, 80°C | 30 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| -40°C | 300 | 260 | MPa | |
| 23°C | 220 | 140 | MPa | |
| 80°C | 115 | 90.0 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Break, -40°C | 3.5 | 3.0 | % | |
| Break, 23°C | 3.5 | 3.5 | % | |
| Break, 80°C | 5.0 | 5.0 | % | |
| Flexural Modulus | ISO 178 | |||
| -40°C | 16100 | 14300 | MPa | |
| 23°C | 13800 | 8100 | MPa | |
| 80°C | 7100 | 5000 | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 385 | 325 | MPa | |
| 23°C | 360 | 230 | MPa | |
| 80°C | 190 | 130 | MPa | |
| Compressive Stress | ISO 604 | |||
| -40°C | 280 | 230 | MPa | |
| 23°C | 220 | 140 | MPa | |
| 80°C | 110 | 80.0 | MPa | |
| Shear Strength (23°C) | 100 | 250 | MPa | ASTM D732 |
| Taber Abrasion Resistance (1000 Cycles) | 0.350 | -- | mg | ISO 9352 |
| Coefficient of Friction - vs. Metal 3 | 0.150 | -- | Suzuki Method |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 16 | 18 | kJ/m² | |
| 23°C | 19 | 24 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -40°C | 120 | 140 | kJ/m² | |
| 23°C | 130 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 225 | -- | °C | ISO 75-2/B |
| Melting Temperature | 225 | -- | °C | DSC |
| CLTE - Flow | 2.0E-5 to 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1400 | -- | J/kg/°C | |
| Thermal Conductivity | 0.40 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | Without Lubrication |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ABS 546P | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Witcom PA6 2009/142 | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| ADDINYL B2 ZV40 | ADDIPLAST | Nylon 6 | ADDINYL |
| Sylvin 9940-60 Orange 591 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NYLOY® CM-5000 8045B1 | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |