Braskem PP R352-08R
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | Braskem Europe GmbH |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a4RRG1_Braskem-PP-R352-08R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Braskem R352-08R Polypropylene Resin is a controlled rheology modified Random Copolymer Polypropylene developed for the manufacturing of cast film for quality packaging applications. Braskem R352-08R Polypropylene Resin does not contain slip and antiblock additives. Applications for Braskem R352-08R Polypropylene Resin:
Regulatory Information Braskem R352-08R Polypropylene Resin should comply with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, Injection Molded) | 22.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, Injection Molded) | 14 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 700 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 50 µm, Cast Film | 410 | MPa | |
| 1% Secant, TD : 50 µm, Cast Film | 420 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 47.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 29.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 450 | % | |
| TD : Break, 50 µm, Cast Film | 590 | % | |
| Dart Drop Impact (50 µm, Cast Film) | 650 | g | ISO 7765-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C, Injection Molded | 3.0 | kJ/m² | |
| 23°C, Injection Molded | 8.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 75.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature 2 | 127 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 85 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 1.4 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® B220MN | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| Sindustris POM N110WR | Sincerity Australia Pty Ltd. | Acetal (POM) Homopolymer | Sindustris POM |
| Zythane® 8090AM | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| Halene H HD T9 | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| IROSTIC® S 6148 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |