Ebalta SG 130 L / PUR 11
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a3ZAI2_Ebalta-SG-130-L-PUR-11.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This is a Polyurethane system. Material should be carefully stirred up/shaked before use. Filler content and sales units are on the separate mixing table noted. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 65 to 69 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 900 to 1100 | MPa | ISO 178 |
| Flexural Stress | 37.0 to 43.0 | MPa | ISO 178 |
| Compressive Stress | 31.0 to 37.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 16 to 24 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Martens Temperature | 40 to 46 | °C | DIN 53458 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 91 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.10 | g/cm³ | |
| Viscosity (25°C) | 0.050 to 0.10 | Pa·s | |
| Curing Time (20°C) | 0.50 to 1.5 | hr | |
| Pot Life 1(20°C) | 5.0 to 7.0 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO F-3900H | Prime Polymer Co., Ltd. | PP Homopolymer | PRIME TPO |
| SCHULADUR® A GF30 | A. Schulman Inc. | PBT | SCHULADUR® |
| SUPREME PP SP5665 | Supreme Petrochem Ltd. | PP, Unspecified | SUPREME PP |
| Double Elephant SX-303 | Suzhou Double Elephant Optical Material Co., LTD. | Acrylic (PMMA) | Double Elephant |
| Edgetek™ ET6000-5019 HI BLACK | PolyOne Corporation | Nylon 6 | Edgetek™ |