FRblend® PA66-1301
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Colour Image Plastic Compound Sdn. Bhd. (CIPC) |
| Trademark: | FRblend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a37Crk_FRblend-PA66-1301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FRblend® PA66-1301 is 25% glass fiber reinforced, flame retardant polyamide 66 compound. This grade offers ignition resistance, balance of strength and excellent processing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.4 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12200 | MPa | ASTM D638 |
| Tensile Strength | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 8690 | MPa | ASTM D790 |
| Flexural Strength | 239 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 94 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 4.00 mm) | 250 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michimid K4100 | API Polymers, Inc. | Nylon 6 | Michimid |
| NILENE® P10 K20T | Taro Plast S.p.A. | PP Homopolymer | NILENE® |
| Fainplast PVC HGKT 84/1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| HIPOL™ F401 | Mitsui Chemicals, Inc. | PP Homopolymer | HIPOL™ |
| LNP™ THERMOCOMP™ GF006 compound | SABIC Innovative Plastics | PSU | LNP™ THERMOCOMP™ |