LNP鈩?STAT-KON鈩?DEP23FXC compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a1xlEo_LNP-STAT-KON-DEP23FXC-compound-41279.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DEP23FXC is a compound based on Polycarbonate resin containing Silicone, Carbon Fiber, PTFE. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound DCL-4523 SM HP Product reorder name: DEP23FXC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.27 | % | ISO 294-4 |
| Flow : 24 hr | 0.16 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.12 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10500 | MPa | ASTM D638 |
| -- | 10200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 121 | MPa | ASTM D638 |
| Break | 123 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.0 | % | ASTM D638 |
| Break | 1.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9100 | MPa | ASTM D790 |
| -- | 10300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 187 | MPa | ASTM D790 |
| -- | 186 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 2 | 7.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 410 | J/m | ASTM D4812 |
| 23°C 3 | 27 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 16.1 | J | ASTM D3763 |
| -- | 3.19 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 137 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 to 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2184 | RTP Company | PEI | RTP |
| Michimid K4100GF33-02 | API Polymers, Inc. | Nylon 6 | Michimid |
| RJM TPS-T 35A | RJM International, Inc. | TPE | RJM |
| Westlake ECTFE Film | Westlake Plastics Company | ECTFE | Westlake |
| APICAL 200AV | Kaneka Corporation | Film, PI | APICAL |