XIRAN® SM200
| Category: | SMA , Styrene Maleic Anhydride |
| Manufacturer: | Polyscope Polymers BV |
| Trademark: | XIRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a1wnal_XIRAN-SM200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
XIRAN® SM200 are SMA (styrene maleic anhydride) based injection molding compounds with:
Application areas XIRAN® SM200 is a injection molding compound designed for applications with high stiffness- strength. These products are very suitable for painted and foamed parts, high temperature resistance and precision parts with high shot to shot consistency. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 22 | g/10 min | ISO 1133 |
| Spiral Flow 1 | 32.0 | cm | Internal Method |
| Molding Shrinkage 2 | Internal Method | ||
| Across Flow | 0.61 | % | |
| Flow | 0.25 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 32.0 | MPa | |
| Break | 30.0 | MPa | |
| Tensile Strain (Break) | 18 | % | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Stress | 62.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 7.0 | kJ/m² | |
| 23°C | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -40°C | 45 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -40°C | 7.0 | kJ/m² | |
| 23°C | 14 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B |
| CLTE | ASTM D696 | ||
| Flow : -30 to 80°C | 4.2E-5 | cm/cm/°C | |
| Transverse : -30 to 80°C | 5.5E-6 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 245 to 275 | °C | |
| Processing (Melt) Temp | < 285 | °C |
| Note Message | |
|---|---|
| 1 . | 2 mm |
| 2 . | Measured according to the Autodesk Mold flow Plastics Labs using a tag mold. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ARCEL® 730B (1.50 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| Delta ATR-2G50 | Delta Polymers | Acetal (POM) Copolymer | Delta |
| KRATON® D1161 J | Kraton Polymers LLC | SIS | KRATON® |
| Karina BLACK PVC COMPOUND -E 105900-48/ 1-B-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TechnoElast A 9000 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |