RX® 852
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | RX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a1kFaX_RX-852.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RX® 852 is a fiberglass reinforced phenolic novolac compound, with good dimensional stability and good strength at elevated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.86 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.10 | % | ISO 2577 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 90 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Compression Molded) | 70.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 19000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 130 | MPa | ISO 178 |
| Compressive Stress | 215 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (Compression Molded) | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 225 | °C | |
| 1.8 MPa, Annealed | > 282 | °C | |
| CLTE | ASTM E831 | ||
| Flow | 2.3E-5 | cm/cm/°C | |
| Transverse | 4.2E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.68 | W/m/K | ASTM C518 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 13 | kV/mm | ASTM D149 |
| Arc Resistance | 180 | sec | ASTM D495 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-3100 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Telcar® SGI60140 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| ACCUCOMP™ ABS846HL | ACLO Compounders Inc. | ABS | ACCUCOMP™ |
| EMPILON® HA80 | EMPILON | SEBS | EMPILON® |
| LNP™ STAT-KON™ MD000IS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |