Xuchuan 1003/B-5301
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Xuchuan Chemical (Suzhou) Co., Ltd |
| Trademark: | Xuchuan |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a1Z4Az_Xuchuan-1003-B-5301.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Xuchuan 1003/B-5301 is a Thermoplastic Polyurethane Elastomer (Polyether) (TPU-Polyether) product. It is available in Asia Pacific. Primary characteristic: good weather resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density | 0.500 to 0.600 | g/cm³ | |
| Density | |||
| A-1003 : 40°C | 1.010 to 1.020 | g/cm³ | |
| B-5301 : 40°C | 1.080 to 1.200 | g/cm³ | |
| Viscosity | |||
| A-1003 : 40°C | 300 to 800 | mPa·s | |
| B-5301 : 40°C | 300 to 600 | mPa·s |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Akron Abrasion | 0.0500 to 0.100 | cm³/1.61 km |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time | 7.0 to 9.0 | sec | |
| End of Rise Time | 1.0 to 1.2 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Free Rise Foam Density | 240 to 280 | kg/m³ | |
| Hydrolysis Strength Retention (70°C) 1 | > 95 | % | |
| Preheat Temperature | |||
| Part A | 50 to 60 | °C | |
| Part B | 60 to 70 | °C | |
| Preheat Time | |||
| Part A | 2.0 to 4.0 | hr | |
| Part B | 10.0 to 15.0 | hr | |
| Processing Temperature | |||
| Part A | 30 to 35 | °C | |
| Part B | 35 to 40 | °C | |
| Resilience | 30 to 40 | % |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 55 to 75 |
| Elastomers | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Break) | 3.30 to 5.50 | MPa | |
| Tensile Elongation (Break) | 280 to 350 | % | |
| Tear Strength | 11.0 to 20.0 | kN/m |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 120 | ||
| Demold Time | 10 to 15 | min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 35.0 to 45.0 | °C |
| Note Message | |
|---|---|
| 1 . | 168 hr, 95% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 71 T 20 | Plastcom | PP, Unspecified | SLOVALEN® |
| Synthos EPS® 1325F/PL | Synthos S.A. | PS (EPS) | Synthos EPS® |
| Celanex® XFR 4840 | Celanese Corporation | PBT | Celanex® |
| DOMAMID® 66G25V0P 1001 A | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Hyundai EP Adhesives LE851P/1002 | HYUNDAI EP Co., Ltd. | PE, Unspecified | Hyundai EP Adhesives |