BMC 620M
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Bulk Molding Compounds, Inc. |
| Trademark: | BMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | a0gtIC_BMC-620M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BMC 620M molding compound is a mineral filled, glass-fiber-reinforced polyester compound suitable for compression, and stuffer injection mo lding It is characterized by high impact strength, good moldability, excellent overall electrical properties and flame resistance. Typical applications include phase separators circuit breaker housings, and applications requiring the properties of Military specification Mil-M-14G Type MAI-60. Although BMC 620M was designed to meet this specification, it has not been submitted for QPL recognition. BMC 620M molding compound is produced in a range of industrial colors, and is supplied in bulk form only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.86 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Compression Molded) | 0.15 to 0.25 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.13 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 35 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Compression Molded) | 62.1 | MPa | ASTM D638 |
| Flexural Strength (Compression Molded) | 152 | MPa | ASTM D790 |
| Compressive Strength | 179 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 14 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 5.20 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 0.020 | ASTM D150 | |
| Arc Resistance | 185 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 500 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-0 | ||
| 3.18 mm | V-0 | ||
| 6.35 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 138 to 166 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XANTAR® MX 1021 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| DAI-EL™ G-702 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Evolue™ SP2030 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| Karina GRAY PVC COMPOUND -E 830-18/ 99-CRM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ZEONEX® K26R | Zeon Corporation | COP | ZEONEX® |