GETILAN GPE/134
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZziNGy_GETILAN-GPE-134.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GETILAN : is the trade-mark of our crosslinkable polyolefinic compounds. GETILAN GPE/134 : high density chemically crosslinkable polythene for insulated aerial cables. It is a conveniently grafted polythene able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/203 HSL. REACTION BETWEEN GRAFTING AND CATALYST: These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 96/4 Certify : ISO 6722 Class D*, FIAT 7.Z8220 T4* |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 0.20 - 0.60 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 20.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 450 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 1(175°C, 240 hr) | 10 | % | ISO 6722 |
| Change in Tensile Strain at Break in Air 2(175°C, 240 hr) | -20 | % | ISO 6722 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 3 | IEC 60811 | ||
| 200°C | % | IEC 60811 | |
| Residual : 200°C | 0.0 | % | IEC 60811 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 210 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | BS 6622 |
| Additional Information |
|---|
| CROSSLINKING:Crosslinking of the finished product is obtained by: Immersion of the bobbin in hot water at 85/90 °C f or two hours (up to 3 mm thickness) Steam treatment at 0.15 bar for 5/6 hours. Air crosslinking at natural temperatures and moisture, after a right number of days depending on climatic conditions, is possibile. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 165 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 205 | °C | |
| Die Temperature | 225 | °C |
| Note Message | |
|---|---|
| 1 . | Test Method: ISO 6722 Class D |
| 2 . | Test Method: ISO 6722 Class D |
| 3 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bapolene® 82 | Bamberger Polymers, Inc. | PET | Bapolene® |
| Aropol™ Q 67700 resins | Ashland Performance Materials | Polyester, TS | Aropol™ |
| Di-Pak™ R-4525/7 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| ELASTOSIL® R 401/70 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Karina BLACK PVC COMPOUND 753-48/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |