Kinta FR3600A
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Kinta Technology (Hong Kong) Co., Ltd. |
| Trademark: | Kinta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZzXBtA_KintaFR3600A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kinta FR3600A is an acrylonitrile butadiene styrene (ABS) product,. It is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.30 - 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 35.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 15 | % | ASTM D638 |
| Flexural Modulus 3 | 2000 | MPa | ASTM D790 |
| Flexural Strength 4 | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 20.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 80.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.6 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70 - 80 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 200 - 210 | °C | |
| Middle Temperature | 205 - 210 | °C | |
| Front Temperature | 200 - 210 | °C | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 40 - 80 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 20 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fixmaster Stainless Steel Putty | Loctite® | Epoxy | Fixmaster |
| Formolene® 3335N | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |
| INNOPOL® PP CS 2-2130 TA | Inno-Comp Ltd. | PP Impact Copolymer | INNOPOL® PP |
| Karina GRAY PVC COMPOUND 600D18/136-A-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hifax TYC 1229P | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |