TAROMID A 280 H G6 X0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZyKBDl_TAROMID-A-280-H-G6-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66 medium viscosity, 30% glass fiber reinforced, UL94 V0 self extinguishing, heat stabilized, very good flame proofing also at low thickness. High mechanical and thermal properties, low shrinkage and high dimensional stability, high tracking resistance. Material PBDE/PBDF free. UL94 V0 approved - All color at 0,88 mm - NC,BK, thickness 0,75 mm - UL 746B approved - CTI UL94 class 1. Available: different colors, release agent (W). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 to 1.58 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Across Flow : 3.20 mm | 0.45 to 0.75 | % | |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.50 | % | |
| Saturation, 23°C | 4.5 | % | |
| Granule Humidity | < 0.15 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 145 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 9000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 200 | MPa | ISO 178 |
| Break | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 7.2 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 75 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 240 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 240 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 2 | 100 | °C | UL 746B |
| -- 3 | 120 | °C | UL 746B |
| -- 4 | 140 | °C | UL 746B |
| -- 5 | 140 | °C | UL 746B |
| -- 6 | 140 | °C | UL 746B |
| -- 7 | 180 | °C | IEC 60216 |
| Vicat Softening Temperature | 242 | °C | ISO 306/B50, ASTM D1525 8 |
| Ball Pressure Test (205°C) | Pass | VDE 0470 | |
| Melting Temperature | 250 to 256 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 2.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 26 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | > 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm, Natural, Black | V-0 | ||
| 0.880 mm, All Colors | V-0 | ||
| Glow Wire Flammability Index (1.20 mm) | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.20 mm) | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 270 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | M. with imp.0,75 mm |
| 3 . | M. with imp. 3 mm |
| 4 . | E. 0,75 mm |
| 5 . | M. w/o imp. 3 mm |
| 6 . | M. w/o imp.0,75 mm |
| 7 . | Short Term |
| 8 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PC 71 T 15 | Plastcom | PP Copolymer | SLOVALEN® |
| Jam HDPE HM8355 | Jam Petrochemical Company | HDPE | Jam HDPE |
| Lifolit® SG 45.1095/1 NP | ELASTO | PVC, Flexible | Lifolit® |
| LUVOCOM® 80-8572/BL | LEHVOSS Group | Acetal (POM) Copolymer | LUVOCOM® |
| Sylvin 6168-80 Red 6204 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |