DIC.PPS FZ-3360-M1
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zy7mzr_DIC-PPS-FZ-3360-M1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DIC.PPS FZ-3360-M1 is a polyphenylene sulfide (PPS) product, which contains glass fiber reinforced materials. It can be processed by injection molding and is available in North America or Asia Pacific. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | ASTM D955 |
| Transverse flow | 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 100 | ASTM D785 | |
| Class r | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 30000 | MPa | ASTM D638 |
| Tensile Strength | 125 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 28000 | MPa | ASTM D790 |
| Flexural Strength | 170 | MPa | ASTM D790 |
| Compressive Strength | 120 | MPa | ASTM D695 |
| Coefficient of Friction | ASTM D1894 | ||
| With Metal-Dynamic | 0.35 | ASTM D1894 | |
| With metal-static | 0.35 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 40 | J/m | ASTM D256 |
| Unnotched Izod Impact | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE - Flow (-30 to 100°C) | 1.7E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 8.0E-3 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 190 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value shown for Comparative Track Index, UL 746, was tested in accordance with ASTM D3638.Flexural Elongation @ Break, ASTM D790: 0.7% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 300 - 340 | °C | |
| Middle Temperature | 300 - 340 | °C | |
| Front Temperature | 300 - 340 | °C | |
| Mold Temperature | 120 - 150 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP6928 D88 | Spartech Polycom | PP, Unspecified | Spartech |
| Multilon® TN-7100F | TEIJIN LIMITED | PC+ABS | Multilon® |
| Capran® 518 LL | Honeywell | Nylon 6 | Capran® |
| ESPRENE EPDM 5527F | Sumitomo Chemical Co., Ltd. | EPDM | ESPRENE EPDM |
| LNP™ STAT-LOY™ NX03583 compound | SABIC Innovative Plastics | PC+ABS | LNP™ STAT-LOY™ |