Menzolit® SMC 1000
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZxsXys_Menzolit-SMC-1000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 1000 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens. Menzolit® SMC 1000 is a special SMC for hydrolysis resistant applications. The glass level has been selected to combine good mouldability with good strength and stiffness properties. Typical applications are components facing exposure to water or moisture. This may be housings, covers and similar components exposed to a tropical climat or humid plant environment causing extensive immersion in water or exposure to high humidity. Sectional watertank panels are another very typical application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.70 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.080 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 60.0 | MPa | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 8000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 65 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 150 | °C | Internal Method |
| Glass Transition Temperature | 145 | °C | DSC |
| CLTE - Flow | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Glow Bar | Level BH 2 <= 30 | IEC 60707-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 150 | °C | |
| Injection Pressure | 8.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 1.8 | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| Bayblend® FR3012 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Huafon T31 | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| INEOS PP L25Zh00 | INEOS Olefins & Polymers USA | PP Impact Copolymer | INEOS PP |
| Eraclene® BB 76 | Versalis S.p.A. | HDPE | Eraclene® |