Next PPS PPSG65-01BK
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zxn7Tx_Next-PPS-PPSG65-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Polyphenylene Sulfide Glass Fiber Reinforced Black Compound Product Applications High Performance plactic materials that are used a wide spectrum of applications Appliance, Automotive, Electric/Electronics, industrial & medical Technology etc Benefits Good combination between Mechanical and electrical properties. Exceptional degree of inherent thermal stability, chemical resistance & flame resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.95 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | |
| Across Flow | 0.20 | % | |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.020 | % | |
| Saturation 1 | 4.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 100 | ||
| R-Scale | 110 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18000 | MPa | ASTM D638 |
| Tensile Strength | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Flexural Modulus | 17500 | MPa | ASTM D790 |
| Flexural Strength | 205 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 88 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 280 | °C | |
| 1.8 MPa, Unannealed | 270 | °C | |
| Melting Temperature | 285 | °C | ASTM D2117 |
| RTI Elec | 240 | °C | UL 746 |
| RTI Imp | 220 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 22 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 130 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 290 to 300 | °C | |
| Middle Temperature | 310 to 320 | °C | |
| Front Temperature | 310 to 320 | °C | |
| Mold Temperature | 135 to 149 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Footwear GF-3161PNU | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Footwear |
| Moplen EP340M | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| TOTAL Polyethylene LDPE FE 8004 | TOTAL Refining & Chemicals | LDPE | TOTAL Polyethylene |
| Grilon® CF 6 S | EMS-GRIVORY | Nylon 6/12 | Grilon® |
| Hapweld™ 36 | Hapco Inc. | TP, Unspecified | Hapweld™ |