Witcom PC 3C-EM-MR Black
| Category: | PC , Polycarbonate |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZvrHGW_Witcom-PC-3C-EM-MR-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PC 3C-EM-MR Black is a polycarbonate (PC) product that contains a 15% carbon fiber reinforced material. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.10 - 0.30 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | < 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 - 4.0 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 190 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 9.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 135 | °C | ISO 75-2/A |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 - 320 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-10190 X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Tarnoform® 300 HI2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| Chemlon® 130 G | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| OnForce™ LFT NN-60LGF/000 HS UV Black | PolyOne Corporation | Nylon 66 | OnForce™ LFT |
| POLYFLAM® HSF 36 | A. Schulman Europe | PS (GPPS) | POLYFLAM® |