EPO-TEK® B9021-6
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZuocrE_EPO-TEK-B9021-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A single component, B-stageable epoxy paste for semiconductor, microelectronics, and optical assemblies. It can be used in hybrid assemblies for lid-sealing and substrate attach. For opto-packaging, it can be used as the main gasket seal of glass plates in LCDs, or for sealing filter windows onto opto-sensors. It is a higher viscosity version of EPO-TEK® B9021-1. |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Dry Time | < 1.0 | day |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 311 | °C | |
| Die Shear Strength - >5 kg (23°C) | 11.7 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 160 | °C | |
| Intermittent | -55 to 260 | °C | |
| Storage Modulus (23°C) | 1.28 | GPa | |
| Thixotropic Index | 6.60 | ||
| Weight Loss on Heating (200°C) | 5.5 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | 80.0 | °C | |
| CLTE - Flow | |||
| -- 1 | 3.2E-5 | cm/cm/°C | |
| -- 2 | 3.7E-5 | cm/cm/°C |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Shelf Life 3 | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | Cream | ||
| Density | 1.23 | g/cm³ | |
| Viscosity 4(23°C) | 15 to 32 | Pa·s | |
| Curing Time | |||
| 75°C 5 | 0.50 | hr | |
| 150°C | 1.0 | hr | |
| Pot Life 6 | 40000 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 68 | ||
| Lap Shear Strength (23°C) | 8.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Below Tg |
| 2 . | Above Tg |
| 3 . | Refrigerated |
| 4 . | 10 rpm |
| 5 . | Pre-cure |
| 6 . | Closed Container |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sasol Polymers PE LT033 (Film Extrusion) | Sasol Polymers | LDPE | Sasol Polymers PE |
| Arnite® TV4 261 /G -99.99.99 | DSM Engineering Plastics | PBT | Arnite® |
| Clariant PBT PBT-1300 | Clariant Corporation | PBT | Clariant PBT |
| Hostacom G3 N01 L303613 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| Sylvin 9048-65 CLEAR | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |