SCHULABLEND® (ABS/PA) M/MK 6501 U
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + PA |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zudm39_SCHULABLENDABSPAMMK6501U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS/PA6 blend with high impact strength, UV stabilised, low emission |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 7.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 40.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 42.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 90 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 18 | kJ/m² | ISO 179/1eA |
| 23°C | 80 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 65.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 125 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.6 mm) | HB | IEC 60695-11-10, -20 | |
| Flammability | mm/min | FMVSS 302 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Processing (Melt) Temp | 230 - 270 | °C | |
| Mold Temperature | 40 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-50/30/FR BK3585 | Techmer Engineered Solutions | PC | TES |
| VICTREX® PEEK 150GL20 | Victrex plc | PEEK | VICTREX® PEEK |
| Nylfor® 64S1303HO 0001 | SO.F.TER. SPA | Nylon 6 | Nylfor® |
| Neoflex™ 7070 | Zylog Plastalloys Pvt. Ltd. | TPE | Neoflex™ |
| LNP™ LUBRICOMP™ RCP36 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |