InnoPlus HD2200JP
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZuQtTH_InnoPlus-HD2200JP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| InnoPlus HD1600JP and HD2200JP are high density polyethylene which can be processed in either injection or compression molding. Both grades have excellent organoleptic properties which prevent unpleasant odor and taste from cap or closure to transfer to water. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.961 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (25% Igepal, F50) | 6.00 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 30.4 | MPa | |
| Break | 20.6 | MPa | |
| Tensile Elongation (Break) | > 1000 | % | ASTM D638 |
| Apparent Bending Modulus | 1080 | MPa | ASTM D747 |
| Flexural Modulus | 1420 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 126 | °C | ASTM D1525 2 |
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Temperature | 140 to 165 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 to 200 | °C | |
| Middle Temperature | 170 to 200 | °C | |
| Front Temperature | 170 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | Complete break |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M800U (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| SCHULATEC® PEEK GF 30 NV 12 | A. Schulman Europe | PEEK | SCHULATEC® |
| Nypol® PA B3 G15 P3 NTLA010 NT313 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| CYCOLOY™ C2950HF resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| NORYL™ FE1520PW resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |