Fortron® MT9141L4 DW
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Celanese Corporation |
| Trademark: | Fortron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZuI6cO_Fortron-MT9141L4-DW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fortron MT9141L4 DW is a 40% glass-reinforced PPS that has excellent heat and chemical resistance, inherently flame-retardant, high hardness and a good balance of strength and stiffness. This grade exhibits low flash and is typically used in applications with thicker walls and shorter flow lengths. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.40 - 0.60 | % | ISO 294-4 |
| Flow direction | 0.20 - 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 195 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 14800 | MPa | ISO 178 |
| Flexural Stress 1 | 290 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 53 | kJ/m² | ISO 179/1eU |
| 23°C | 53 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 270 | °C | ISO 75-2/A |
| Glass Transition Temperature 2 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 280 | °C | ISO 11357-3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.380 mm | V-0 | UL 94 | |
| 1.50 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 290 - 300 | °C | |
| Middle Temperature | 310 - 320 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 310 - 330 | °C | |
| Processing (Melt) Temp | 330 - 340 | °C | |
| Mold Temperature | 140 - 160 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 330 to 340°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | Break |
| 2 . | 10°C/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPE EE-1250N | Teknor Apex Company | TPE | Sarlink® TPE |
| TOTAL Polypropylene PPH 3740WR | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Elastron® G G400.A80.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Plenco 03356 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |
| Badamid® PPA CF30 | Bada AG | PPA | Badamid® |