LNP™ STAT-KON™ JE006E compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZuDlx8_LNP-STAT-KON-JE006E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-KON JE006E is a compound based on Polyethersulfone resin containing 30% Carbon Fiber. Added features of this grade include: Easy Molding, Electrically Conductive. Also known as: LNP* STAT-KON* Compound JC-1006 EM Product reorder name: JE006E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.17 | % | |
| Across Flow : 24 hr | 0.55 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.29 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.48 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 25800 | MPa | ASTM D638 |
| -- | 25200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 225 | MPa | ASTM D638 |
| Break | 215 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.4 | % | ASTM D638 |
| Break | 1.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 15500 | MPa | ASTM D790 |
| -- 5 | 21000 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 309 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 265 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 77 | J/m | ASTM D256 |
| 23°C 7 | 7.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D4812 |
| 23°C 8 | 36 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.6 | J | ASTM D3763 |
| -- | 3.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 223 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 225 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 218 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 219 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 9.0E-6 | cm/cm/°C | |
| Transverse : -30 to 30°C | 3.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® 2210HS BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |
| Starflam RFB247EX | Eurostar Engineering Plastics | Nylon 66/6 | Starflam |
| TOTAL Polyethylene Lotrène® Q1018 N | TOTAL Refining & Chemicals | LLDPE | TOTAL Polyethylene |
| Trexprene® D50BW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| RTP 199 X 138766 Z EG | RTP Company | PP, Unspecified | RTP |