Andur M-22 (94% 1,4BD, 6% TMP)
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZuCpwS_Andur-M-22-94-1-4BD-6-TMP-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur M-22 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 83 | ASTM D2240 | |
| Shaw D | 34 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 2% strain | 0.552 | MPa | ASTM D695 |
| 5% strain | 1.14 | MPa | ASTM D695 |
| 10% strain | 2.21 | MPa | ASTM D695 |
| 15% strain | 3.28 | MPa | ASTM D695 |
| 20% strain | 4.41 | MPa | ASTM D695 |
| 25% strain | 5.79 | MPa | ASTM D695 |
| 50% strain | 11.7 | MPa | ASTM D695 |
| Taber Abrasion Resistance | 7.00 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 4.48 | MPa | ASTM D412 |
| 300% strain | 11.0 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 51.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 550 | % | ASTM D412 |
| Compression Set | 35 | % | ASTM D395 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 4.0 - 6.0 | min | |
| Demold Time | 60 | min |
| Additional Information |
|---|
| Die C Tear, ASTM D1004: 450 pliAverage Split Tear, ASTM D1938: 235 pliStoichiometry Curative Level: 97%Break Set, ASTM D412-80: 8%NBS Abrasion: 285% Rubber StandardParts of curative per 100 parts Andur M-22, 6.5% NCO: 6.76 parts by weightParts of curative per 100 parts Andur M-22, 6.55% NCO: 6.81 parts by weightParts of curative per 100 parts Andur M-22, 6.6% NCO: 6.87 parts by weightParts of curative per 100 parts Andur M-22, 6.65% NCO: 6.92 parts by weightParts of curative per 100 parts Andur M-22, 6.7% NCO: 6.97 parts by weightMix Temperature: Andur M-22: 194-212°F Curative 1,4BD/TMP: 77-158°F Stability: Ambient Temperature, 25°C: 6 Months Melting Temperature, 60°C: 1 Month Processing Temperature, 90°C: 12 Hours Processing Temperature, 105°C: 3 Hours |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 90.0 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nylfor® A2 GF/30 FR2/3A NATURALE | SO.F.TER. SPA | Nylon 66 | Nylfor® |
| Ebalta GM 956 / Comp. A+B | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Kumho ABS BM-530 | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| LUVOCOM® 1-8934/BL/L | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| PENTAMID B GK15 H natural | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |