ASTALOY™ MB2106
| Category: | PC , Polycarbonate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zt78iu_ASTALOY-MB2106.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALOY™ MB2106 is an alloy of Polycarbonate (PC) and Polyethylene Terephtalate (PET) which is suited to injection moulding applications. Offering an exceptional combination of toughness, heat resistance, chemical resistance, rigidity, UV resistance and and processability, typical applications include automotive exterior door handles, outside use electric pump housings, automotive bumper bars and electrical switch junction boxes. Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ MB2106U ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1(3.00 mm) | 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(3.20 mm) | 62.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 120 | % | ASTM D638 |
| Flexural Modulus 4(6.40 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 5(6.40 mm) | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 850 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | > 85.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 148 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 131 | °C | |
| CLTE - Flow | 5.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Dielectric Constant | 2.10 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 125 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 245 to 265 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 275 to 295 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 110 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 100 mm diameter disc |
| 2 . | 20 mm/min |
| 3 . | 20 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® R200 GF 18 | Ravago Group | Nylon 6 | Ravamid® |
| TRIEL® 5500 | Samyang Corporation | TPEE | TRIEL® |
| APEX® 3600-75NT | Teknor Apex Company | PVC, Flexible | APEX® |
| POLIMAXX 2500PC | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| NILAMID® XS1 GF60 | Nilit Plastics | Nylon, Unspecified | NILAMID® |