OP - PC - Unfilled 20-FDA
| Category: | PC , Polycarbonate |
| Manufacturer: | Oxford Polymers |
| Trademark: | OP - PC - Unfilled |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZsuQ92_OP---PC---Unfilled-20-FDA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OP-PC-Unfilled 20-FDA is a polycarbonate (PC) material,. This product is available in North America and is processed by injection molding. The main features of OP-PC-Unfilled 20-FDA are:
OP-PC-Unfilled 20-FDA's typical application areas are: food contact applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 62.1 | MPa | ASTM D638 |
| Fracture | 65.5 | MPa | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength | 92.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (4°C) | 640 | J/m | ASTM D256 |
| Dart Drop Impact | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 129 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 124 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-2 | UL 94 | |
| 3.18 mm | V-2 | UL 94 |
| Additional Information |
|---|
| Melt Mass - Flow Rate (MFR), ASTM D1238, 300°C/1.2kg: 20 to 25 g/10 min |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 - 124 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 249 - 271 | °C | |
| Middle Temperature | 260 - 282 | °C | |
| Front Temperature | 271 - 293 | °C | |
| Processing (Melt) Temp | 266 - 293 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Prime Series NST35-01NC | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |
| Cheng Yu 3265 | Cheng Yu Plastic Company Limited | TPE | Cheng Yu |
| HiFill® PA6 0303 B | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| TABOREN® PC 42 B 35-630 | SILON s.r.o. | PP Copolymer | TABOREN® |
| Durethan® C 38 FA 000000 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |