Elvakon® 4421
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Holland BV |
| Trademark: | Elvakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zr101v_Elvakon4421.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultra low gloss acrylic capstock Lucite® Elvakon® 4421 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 36.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 16 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Flexural Stress | 64.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.1 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 3.1 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 93.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 83.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 97.0 | °C | ISO 306/A |
| -- | 87.0 | °C | ISO 306/B |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 10 - 15 | Internal method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205.3 TFE 5 HS L | RTP Company | Nylon 66 | RTP |
| SABIC® HDPE CC1053 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Bapolene® 2035 | Bamberger Polymers, Inc. | HDPE | Bapolene® |
| LUVOCOM® 1301-8558 | LEHVOSS Group | PPS | LUVOCOM® |
| Durethan® BKV 30 W1 000000 | LANXESS GmbH | Nylon 6 | Durethan® |