NYCOA 512 is a fast cycling nucleated and lubricated Nylon 6 used for injection molding applications. This material features outstanding processability, chemical resistance, and an excellent balance of mechanical properties. NYCOA 512 is recognized by Underwriters Laboratories to standard UL 94-V-2 for thickness as low as 0.7 mm. It is also listed by the National Sanitation Foundation (NSF) under standard 61 for use in products that come into contact with food or potable wate Typical applications include plumbing fittings and housings, thin wall molding, toys and hardware items. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.2 | % | ASTM D955 |
| Transverse flow | 1.4 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.7 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 90.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 3 | 2800 | MPa | ASTM D790 |
| Flexural Strength 4 | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 45 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 191 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.3 | °C | ASTM D648 |
| Melting Temperature | 221 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.700 mm) | V-2 | UL 94 |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 221 - 241 | °C | |
| Middle Temperature | 235 - 252 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 254 - 266 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.517 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ABS 1001 | ROMIRA GmbH | ABS | Rotec® ABS |
| Westlake LDPE EM808AA | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| Bynel® 22E757 | DuPont Packaging & Industrial Polymers | EA | Bynel® |
| Latilon 28D K/20 | LATI S.p.A. | PC | Latilon |
| Sumiliteresin® PR-53416 | SBHPP | Phenolic | Sumiliteresin® |