Fibremod™ GD302HP
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZqZ4rw_Fibremod-GD302HP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod GD302HP is a 30 % chemically coupled high performance glass fibre reinforced polypropylene compound intended for injection moulding. This material has an excellent balance between impact strength and stiffness and is easy to process. Applications: Fibremod GD302HP has been developed especially for the automotive industry.
Features:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.3 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Vertical flow direction : 2.00mm | 0.80 | % | Internal method |
| Flow direction : 2.00mm | 0.060 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 5600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, Injection Molded) | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, Injection Molded) | 4.0 | % | ISO 527-2 |
| Flexural Modulus 2(Injection Molded) | 5100 | MPa | ISO 178 |
| Flexural Stress (Injection Molded) | 86.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C, injection molding | 13 | kJ/m² | ISO 179/1eA |
| 23°C, injection molding | 24 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C, injection molding | 60 | kJ/m² | ISO 179/1eU |
| 23°C, injection molding | 65 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C, injection molding | 16 | kJ/m² | ISO 180/1A |
| 23°C, injection molding | 28 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 132 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 - 280 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 to 80°CBack pressure: As low as possibleScrew speed: Low to mediumFlow front speed: 100 to 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 150x80x2 mm |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7500 GF 50 H | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| CP PRYME® Nylon 6 N213HSL | Chase Plastics Services Inc. | Nylon 6 | CP PRYME® Nylon 6 |
| DESLON™ 66 DSC201G9 | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| PLUSTEK RA321G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| MARPOL® COPP 1.5.4 | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |