Ultramid® 8262G HS BK-125
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZpDZLS_Ultramid-8262G-HS-BK-125.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8262G HS BK-125 is a heat stabilized, pigmented black, 20% glass and mineral reinforced PA6 injection molding compound resulting in a balance of engineering properties with excellent dimensional stability, low warp and good resistance to sink mark formation. Applications Ultramid 8262G HS BK-125 is generally recommended for applications such as automotive housings, brackets, hubs, shrouds and roller bearings |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 0.80 | % | |
| Water Absorption | |||
| 24 hr | 1.3 | % | ASTM D570 |
| 23°C, 24 hr | 1.3 | % | ISO 62 |
| Saturation | 7.9 | % | ASTM D570 |
| Saturation, 23°C | 7.9 | % | ISO 62 |
| Equilibrium, 50% RH | 2.2 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5300 | MPa | ISO 527-2 |
| Tensile Strength (Break, 23°C) | 100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C) | 4600 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 160 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 3.3 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 35 | J/m | ASTM D256 |
| -40°C | 3.0 | kJ/m² | ISO 180 |
| 23°C | 4.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 211 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 163 | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | °C | ASTM D3418, ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.45 to 10.3 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Next Nylon 6 Industrial Series NX-02BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Industrial Series |
| COPYLENE® CM350LN | Phillips 66 | PP Impact Copolymer | COPYLENE® |
| Di-Pak™ E-4666-3 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| Polifor® E 3 NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |
| StarClear® 1050-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarClear® |