Latishield 87/28-10A
| Category: | PC , Polycarbonate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latishield |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZpDVLB_Latishield-87-28-10A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMI shielding product based on Polycarbonate (PC). Steel fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 0.75 | % | |
| Flow : 2.00 mm | 0.55 to 0.75 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 12 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C, 3.20 mm) | 65 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 135 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+2 | ohms | ASTM D257 |
| Electromagnetic Reflection | 95 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 265 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Rite® S-1107 | Lubrizol Advanced Materials, Inc. | TPU Alloy | Stat-Rite® |
| APEX® 3085-H | Teknor Apex Company | PVC, Flexible | APEX® |
| Daplen™ KB4436 | Borealis AG | PP, Unspecified | Daplen™ |
| INELEC PA612CF30 | Infinity LTL Engineered Compounds | Nylon 6/12 | INELEC |
| ISPLEN® PP 040 G1E | REPSOL | PP Homopolymer | ISPLEN® |