LNP™ THERMOCOMP™ MF006S compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZozvWk_LNP-THERMOCOMP-MF006S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP MF006S is a compound based on Polypropylene resin containing 30% Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound MFX-1006 HS Product reorder name: MF006S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.60 to 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.90 to 1.1 | % | ASTM D955 |
| Across Flow : 24 hr | 0.98 | % | ISO 294-4 |
| Flow : 24 hr | 0.65 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 14500 | MPa | ASTM D638 |
| -- | 9120 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 81.4 | MPa | ASTM D638 |
| Break | 80.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.8 | % | ASTM D638 |
| Break | 3.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6210 | MPa | ASTM D790 |
| -- | 6800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 131 | MPa | ASTM D790 |
| -- | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 5.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 600 | J/m | ASTM D4812 |
| 23°C 3 | 38 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 158 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 161 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 134 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 141 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.9E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.5E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 4.4E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3570 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Telcar® TL-86-K975-A | Teknor Apex Company | TPE | Telcar® |
| Zythane® 5080A | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| Elexar® EL-8452 | Teknor Apex Company | TPE | Elexar® |
| LARIPUR® LPR 5260 | COIM S.p.A. | TPU-Polyether | LARIPUR® |