GAPEX® HP RPP30EU92BK
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® HP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZnxPoS_GAPEX-HP-RPP30EU92BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX®HP RPP30EU92BK is a polypropylene material, which contains a 30% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. GAPEX®The main features of HP RPP30EU92BK are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.70 | % | ISO 294-4 |
| Flow direction | 0.20 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 84.2 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 8.0 | % | ISO 527-2 |
| Flexural Modulus - Tangent | 5250 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -40°C | 8.2 | kJ/m² | ISO 180/1A |
| 23°C | 15 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 146 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Filler Content, ISO 3451: 30%Flammability, ISO 3795: 18 mm/minMold Shrinkage, ISO 2577, Flow, 48 hr, 23°C: 0.2%Mold Shrinkage, ISO 2577, Across Flow, 48 hr, 23°C: 0.7% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 221 - 238 | °C | |
| Middle Temperature | 227 - 243 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Nozzle Temperature | 232 - 260 | °C | |
| Processing (Melt) Temp | 221 - 238 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 5.08 - 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stirol UPM-0612 L (extra) | JSC CONCERN STIROL | PS (HIPS) | Stirol |
| Sylvin 8260-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Flontech® FT-COND2-2 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| LNP™ STAT-KON™ DEP23FXC compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| Petlon Prime B1-G50-00-BK | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |