EPIMIX PBT GFR 30 NC
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPIMIX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zmone4_EPIMIX-PBT-GFR-30-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EPIMIX PBT, reinforced with 30% of glass fiber, heat stabilized, superior gloss ,lubricated for injection moulding. EPIMIX PBT GFR 30 is used in all sectors of industry, compliance with RoHs derivatives. This product is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.52 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.0 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.30 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 30 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 82 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 8200 | 7900 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 120 | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 2.0 | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 7800 | 7500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 175 | 160 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | 9.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 7.0 | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3 | ||||
| 0.45 MPa, not annealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NuSil CV4-1161-5 | NuSil Technology | Silicone | NuSil |
| Adflex Q 100 F | LyondellBasell Industries | Polyolefin, Unspecified | Adflex |
| APEX® 3801-60NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina WHITE PVC COMPOUND -E 839-10/ 68-Y-CRA | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pibifor® K2 FR7/2H NATURALE | SO.F.TER. SPA | PBT | Pibifor® |