EPO-TEK® EJ2189-LV
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZmCygO_EPO-TEK-EJ2189-LV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Two component, low viscosity, room temperature curing, conductive epoxy. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| Cl- | 201 | ppm | |
| K+ | 2 | ppm | |
| Na+ | 27 | ppm | |
| NH4+ | 53 | ppm | |
| Particle Size | < 45.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 340 | °C | |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 150 | °C | |
| Intermittent | -55 to 250 | °C | |
| Storage Modulus | 1.47 | GPa | |
| Thixotropic Index | 3.30 | ||
| Weight Loss on Heating | |||
| 200°C | 0.34 | % | |
| 250°C | 0.80 | % | |
| 300°C | 1.6 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 40.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 5.2E-5 | cm/cm/°C | |
| -- 3 | 8.9E-5 | cm/cm/°C | |
| Thermal Conductivity | 2.0 | W/m/K |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Amber | ||
| -- 5 | Silver | ||
| Density | |||
| Part B | 0.938 | g/cm³ | |
| Part A | 3.06 | g/cm³ | |
| Viscosity 6(23°C) | 25 to 45 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 240 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 41 | ||
| Lap Shear Strength (23°C) | 9.21 | MPa | |
| Volume Resistivity | |||
| 23°C 7 | < 5.0E-4 | ohms·cm | |
| 23°C 8 | < 5.0E-3 | ohms·cm | |
| 23°C 9 | > 7.0E-3 | ohms·cm | |
| 23°C 10 | < 9.0E-3 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 1 rpm |
| 7 . | 150°C/1 hour cure |
| 8 . | 80°C/3 hours cure |
| 9 . | 25°C/40-60%RH/3 Day cure |
| 10 . | 23°C/72 hours cure |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 AR 15 TFE 15 | RTP Company | PEEK | RTP |
| UNITIKA Nylon 66 BV2120G15 | UNITIKA Plastics Division | Nylon 66 | UNITIKA Nylon 66 |
| ASTAMID™ MA3G3HS | Marplex Australia Pty. Ltd. | Nylon 66 | ASTAMID™ |
| Geon™ Vinyl Wire & Cable WJAX208U | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| INTEGRAL™ 604 | The Dow Chemical Company | Polyolefin, Unspecified | INTEGRAL™ |