LNP™ THERMOCOMP™ RX10405H compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZlWIW0_LNP-THERMOCOMP-RX10405H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RX10405H is a compound based on Nylon 66 resin containing Carbon Fiber. Added feature of this material is: Healthcare. Also known as: LNP* THERMOCOMP* Compound RX10405H Product reorder name: RX10405H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 31000 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 276 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.6 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 24400 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 386 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 256 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE F04660 (Blow moulding) | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Riteflex® 830 | Celanese Corporation | TPC-ET | Riteflex® |
| Dion VER 9100 | Reichhold Chemicals, Inc. | Vinyl Ester | Dion |
| TORZEN® G3300L NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| SABIC® SUPEER™ 8112L | Saudi Basic Industries Corporation (SABIC) | mLLDPE | SABIC® SUPEER™ |