MAGNUM™ 3416NA
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZlLBlM_MAGNUM-3416NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Heat, Low Gloss ABS resin with good practical toughness for injection molded automotive interior applications. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Apparent Density | 0.66 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 220°C/10.0 kg | 8.0 | g/10 min | |
| 230°C/3.8 kg | 2.6 | g/10 min | |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.55 | % | |
| Flow | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2180 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 43.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus | 2260 | MPa | ISO 178 |
| Flexural Stress | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 18 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 20 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 107 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 1(2.00 mm) | 25 | mm/min | ISO 3795 |
| Carbon Emission 2 | 10.0 | µg/g | VDA 277 |
| Fogging 3(100°C) | 94 | % | ISO 6452 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 243 | °C | |
| Middle Temperature | 254 | °C | |
| Front Temperature | 260 | °C | |
| Nozzle Temperature | 254 | °C | |
| Processing (Melt) Temp | 254 to 271 | °C | |
| Mold Temperature | 38.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP520-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| SCANAMID 6 B12^ F30 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Sindustris PC SF1010 | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| LNP™ THERMOCOMP™ RF004XXD compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Formolene® 1104KR | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |