Baytec® MP-090 (HQEE)
| Category: | PUR-Ether/MDI , Polyurethane (Polyether, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zkl2iD_Baytec-MP-090-HQEE-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec MP-090 is a modified diphenylmethane diisocyanate (MDI)-terminated polyether prepolymer based on polypropylene ether glycol (PPG). This prepolymer is used in the manufacture of cast polyurethane elastomers. As with any product, use of Baytec MP-090 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 95 | ASTM D2240 | |
| Shaw D | 56 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 50.0 | mg | ASTM D4066 |
| Compression Deflection | ASTM D575 | ||
| 10% | 5.03 | MPa | ASTM D575 |
| 15% | 7.10 | MPa | ASTM D575 |
| 2% | 0.448 | MPa | ASTM D575 |
| 20% | 9.24 | MPa | ASTM D575 |
| 25% | 11.6 | MPa | ASTM D575 |
| 5% | 2.45 | MPa | ASTM D575 |
| 50% | 41.4 | MPa | ASTM D575 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 9.65 | MPa | ASTM D412 |
| 200% strain | 18.2 | MPa | ASTM D412 |
| 300% strain | 21.5 | MPa | ASTM D412 |
| Tensile Strength (Break) | 28.4 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 350 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 81.8 | kN/m | ASTM D624 |
| Cracking | 21 | kN/m | ASTM D1938 |
| Compression Set (70°C, 22 hr) | 30 | % | ASTM D395 |
| Bayshore Resilience | 29 | % | ASTM D2632 |
| Additional Information |
|---|
| Appearance: Pale yellow liquidNCO: 8.95 to 9.24 wt%Specific Gravity at 80°C: 1.07Specific Gravity at 100°C: 1.06Viscosity at 80°C: 255 mPa-sViscosity at 100°C: 115 mPa-sNCO/OH Ratio: 1.10Stoichiometry: 90% TheoryPrepolymer Temperature: 90 to 100°CExtender Temperature: 100 to 110°CMold Temperature: 90 to 110°CPot Life: 6.5 minDemold: 60 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell Polyamide BJ-33 Impact Modified | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| Ferro PP TPP20AE63BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| Hapflex™ 1036 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| OmniLon™ PA6/6 IM4 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |
| Petrothene® LT523521 | LyondellBasell Industries | HDPE | Petrothene® |