TAROMID B 240 NG4 Y2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZkBIWs_TAROMID-B-240-NG4-Y2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 medium low viscosity 20% glass fibres reinforced, halogen free flame retardant UL94 V2, good flame proofing also at low thickness, good flow and good mechanical properties. High CTI value. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.34 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.55 | % | Internal method |
| Flow direction | 0.45 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | ISO 62 |
| Saturated, 23°C | 6.0 | % | ISO 62 |
| Granule Humidity 1 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 2(850°C) | 20 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus 3 | 5500 | MPa | ISO 178 |
| Flexural Stress 4 | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.7 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 19 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 40 | J/m | ASTM D256 |
| Notched Izod Impact (23°C) | 3.00 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed) | 202 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Ball Pressure Test (175°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 222 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 mm) | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 25 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 1.0 | hr | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1 hr |
| 3 . | 1.0 mm/min |
| 4 . | 1.0 mm/min |
| 5 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synres-Almoco EP 3535 | Synres-Almoco BV | Epoxy | Synres-Almoco |
| TOTAL Polystyrene Compound 853 | TOTAL Refining & Chemicals | PS (IRPS) | TOTAL Polystyrene |
| Nypol® PA A3 G30 HS UV PRTA011 NR395 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| FRblend® PBT-2500 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PBT | FRblend® |
| Hostalen PP H1850 | LyondellBasell Industries | PP Homopolymer | Hostalen PP |