Taitarex® 666
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Taita Chemical Company, Ltd. |
| Trademark: | Taitarex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZioZ3Z_Taitarex-666.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Taitarex® 666 is a High Impact Polystyrene material. It is available in Asia Pacific or North America for injection molding. Important attributes of Taitarex® 666 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D542 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 7.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.18 mm) | 26.5 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C, 3.18 mm) | 45 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| 23°C 2 | 78 | J/m | |
| 23°C 3 | 88 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 4 | 99.0 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Yellowness Index | -3.0 | YI |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Residual Monomer - SM | < 600 | ppm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 160 to 280 | °C | |
| Middle Temperature | 160 to 280 | °C | |
| Front Temperature | 160 to 280 | °C | |
| Mold Temperature | 35.0 to 65.0 | °C | |
| Injection Pressure | 49.0 to 137 | MPa |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1/4"x1/2"x5/2" |
| 3 . | 1/8"x1/2"x5/2" |
| 4 . | 3 mm thick |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Queo™ 0207LA | Borealis AG | Plastomer | Queo™ |
| Ultramid® HPN 9233G HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| EPS Silver® S700R | INEOS Styrenics International SA | PS (EPS) | EPS Silver® |
| LNP™ LUBRICOMP™ DFL36HL compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRICOMP™ |
| LubriOne™ NN-000/15T BK047 | PolyOne Corporation | Nylon 66 | LubriOne™ |