Ateva® 2604A
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZimpUm_Ateva-2604A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for hot melt coating and adhesive, automotive compounding, microcellular crosslinked foam, and molding applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 26.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 84 | ||
| Shore D | 23 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 11.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 760 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 24.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 46.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 76.0 | °C | ASTM D3418 |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210G30 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| NYLOY® UB-0010N-V G55L2B | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| Haysite Plastics H330 | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| Hapcoat™ 3727 | Hapco Inc. | TP, Unspecified | Hapcoat™ |
| HIFOR Xtreme® SC74853 | Westlake Chemical Corporation | LLDPE | HIFOR Xtreme® |