Order Products : sales@su-jiao.com
XENOY™ 6620 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZiHhQg_XENOY6620resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Impact modified, highly chemical resistant polyester/polycarbonate alloy. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.4 - 2.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 43.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 180 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 1720 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 50.0 mm Span) | 64.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 60.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Processing (Melt) Temp | 250 - 290 | °C | |
| Mold Temperature | 55.0 - 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu RTV KE-1830 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Shandong PA1212 GYBMVN | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| TECHNYL® A 221 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| POLYFORT® FPP 1182E | A. Schulman Inc. | PP, Unspecified | POLYFORT® |
| Hifax TYC 258P 9B9 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |