Plexar® PX3236
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Plexar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Zhdv50_Plexar-PX3236.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s). |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm, Blown Film | 11.0 | MPa | |
| TD : Yield, 51 µm, Blown Film | 12.2 | MPa | |
| MD : Break, 51 µm, Blown Film | 28.4 | MPa | |
| TD : Break, 51 µm, Blown Film | 28.8 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 51 µm, Blown Film | 12 | % | |
| TD : Yield, 51 µm, Blown Film | 4.0 | % | |
| MD : Break, 51 µm, Blown Film | 680 | % | |
| TD : Break, 51 µm, Blown Film | 730 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm, Blown Film | 200 | g | |
| TD : 51 µm, Blown Film | 470 | g | |
| Water Vapor Transmission Rate (100% RH, 51 µm, Blown Film) | 6.8 | g/m²/24 hr | ASTM F372 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | > 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU P990 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SILVER® PC2540.HF | Guangdong Silver Age Sci & Tech. Co., Ltd | PC+ABS | SILVER® |
| Nypol® PA A3 T40 HS NTLA013 NR327 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Celanex® 2002-2 | Celanese Corporation | PBT | Celanex® |
| Isoplast® 202 LGF40 ETPU | Lubrizol Advanced Materials, Inc. | ETPU | Isoplast® |