DOW™ LLDPE DNDA-1081 NT 7

Category:	LLDPE , Linear Low Density Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOW™ LLDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ZhZowG_DOW-LLDPE-DNDA-1081-NT-7.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Injection molding

Lids

Excellent processability with good low temperature impact strength and rigidity

Very narrow molecular weight distribution

Complies with U.S. FDA 21 CFR 177.1520 (c)3.1a

Complies with FDA-DMF

Complies with EU, No 10/2011

Complies with CANADIAN HPFB NO OBJECTION (WITH LIMITATIONS)

Consult the regulations for complete details.

DOW DNDA-1081 NT 7 Linear Low Density Polyethylene (LLDPE) Resin is produced using UNIPOL™ PE Process Technology and is intended for highspeed injection molding of thin-walled parts such as downgauged lids. This resin has been designed to have an excellent balance of processability, impact strength, and rigidity.

General Information
Agency Ratings	DMF not rated FDA 21 CFR 177.1520(c) 3.1a HPFB (Canada) No Objection 2 Europe No 10/2011
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.931	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	130	g/10 min	ASTM D1238

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	55		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	11.0	MPa	ASTM D638
Fracture	8.96	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	2.0	%	ASTM D638
Fracture	60	%	ASTM D638
Flexural Modulus - 2% Secant	524	MPa	ASTM D790B

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength ¹	105	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	51.1	°C	ASTM D648
Brittleness Temperature	-23.9	°C	ASTM D746
Vicat Softening Temperature	97.2	°C	ASTM D1525
Melting Temperature (DSC)	126	°C	Internal method
Peak Crystallization Temperature (DSC)	113	°C	Internal method

Additional Information
根据 ASTM D 4976 进行基板模制和测试。

Note Message
1 .	Type s

Resin Grade	Manufacturer	Category	Trademark
RTP ESD 800 TFE 5	RTP Company	Acetal (POM) Copolymer	RTP
APICAL 250AF029	Kaneka Corporation	Film, PI	APICAL
Axiall PVC 8950	Axiall Corporation	PVC, Flexible	Axiall PVC
Karina NATURAL PVC COMPOUND -E V-150 LT	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
POCAN® BF 4409 000000	LANXESS Corporation	PBT	POCAN®