Fibremod™ GB601HP-9502
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZhGNle_Fibremod-GB601HP-9502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fibremod GB601HP-9502 is a special long glass fibre reinforced polypropylene concentrate grade intended for injection moulding and extrusion. This material is designed for the dilution process in combination with special developed dilution polypropylene grades, for example homopolymer HK060AE or copolymer BJ356MO. This combination of concentrate - dilution polypropylene should then be adjusted for a glass fibre content range of 20 - 40 % in the end product. The product is available in standard black 9502. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 127 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 15000 | MPa | ISO 527-2 |
| Tensile Stress | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.1 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 14100 | MPa | ISO 178 |
| Flexural Stress | 195 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 24 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 167 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 164 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 40.0 - 80.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperatrue: 40 - 80 °CMass Temperature: 240 - 280 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G10 272 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| DESLON™ 66 DSC201G3 | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| Kumho ABS H2938L | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| Lupox® SG3250A | LG Chem Ltd. | PBT+PET | Lupox® |
| TECHNYL® A 218HPS V35 BLACK 21N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® RED |