SCHULAMID® PPA GF 33
| Category: | PPA , Polyphthalamide |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZgMhhv_SCHULAMIDPPAGF33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyphthalamid with 33% GF, high stiffness and strength at high temperatures, heatstabilzed, high chemical resistence |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.46 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 13700 | 12000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 195 | 162 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | 1.6 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 45 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 70 | 37 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, annealing, 3.30mm 1 | 297 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 280 | -- | °C | ISO 75-2/A |
| 1.8 MPa, annealed, 3.20mm | 285 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 303 | -- | °C | ISO 306/B |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 310 - 345 | °C | |
| Mold Temperature | 120 - 160 | °C |
| Note Message | |
|---|---|
| 1 . | Thickness 3.2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROPRENE® 1 A35 E1N | Taro Plast S.p.A. | TPV | TAROPRENE® |
| DOMAMID® 66SN | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Globalprene® 3411P | Lee Chang Yung Chemical Industry Corp. | SBS | Globalprene® |
| HiFill FR® PA6 GF15 FR-N | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| LUVOCOM® 1850-7692 VP | Lehmann & Voss & Co. | PBT | LUVOCOM® |