LNP™ THERMOCOMP™ DX07408 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZgG822_LNP-THERMOCOMP-DX07408-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DX07408 is a compound based on Polycarbonate containing Proprietary Filler(s). Added feature of this grade is: UL Rated. Also known as: LNP* THERMOCOMP* Compound DX07408 Product reorder name: DX07408 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.40 | % | |
| Across Flow : 24 hr | 0.60 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10400 | MPa | ASTM D638 |
| -- | 10000 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 120 | MPa | ASTM D638 |
| Yield | 126 | MPa | ISO 527-2/5 |
| Break 3 | 120 | MPa | ASTM D638 |
| Break | 126 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.0 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2/5 |
| Break 5 | 2.0 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 9570 | MPa | ASTM D790 |
| -- 7 | 9100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 173 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 179 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 179 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 100 | J/m | ASTM D256 |
| 23°C 10 | 9.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 580 | J/m | ASTM D4812 |
| 23°C 11 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 17.6 | J | ASTM D3763 |
| -- | 3.48 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 139 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 135 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TP-G15 | Polymer Resources Ltd. | PBT | PRL |
| SuperLite® SL551200-100 (2.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Vibrathane® B836 | Chemtura | PUR-Ether/MDI | Vibrathane® |
| Capilene® T 50 | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| TECHNYL® A 60G1 V30 BLACK 61 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |