Starflex GM1810BE
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Starflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZfySxS_Starflex-GM1810BE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starflex GM1810BE is a pelletized mLLDPE resin for use in applications that require maximum strength and toughness. GM1210BA contains a processing aid, slip and antiblock. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 19 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 19 µm | 186 | MPa | ASTM D882 |
| 1% secant, TD : 19 µm | 193 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 19 µm | 67.6 | MPa | ASTM D882 |
| TD : Break, 19 µm | 59.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 19 µm | 470 | % | ASTM D882 |
| TD : Break, 19 µm | 570 | % | ASTM D882 |
| Dart Drop Impact 1(19 µm) | 600 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 19 µm | 150 | g | ASTM D1922 |
| TD : 19 µm | 260 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 19.1 µm) | 45 | ASTM D2457 | |
| Haze (19.1 µm) | 16 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 232 | °C |
| Extrusion instructions |
|---|
| Blow-up ratio: 1.5 to 3 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GF 25 | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| Celstran® PA6-GF40-03 | Celanese Corporation | Nylon 6 | Celstran® |
| GERMADUR B GF 30 SCHWARZ | Kunststoff-Kontor-Hamburg GmbH | PBT | GERMADUR |
| Polene LDPE JJ 4324 | TPI Polene Public Company Limited | LDPE | Polene LDPE |
| ULTEM™ 2110R resin | SABIC Innovative Plastics | PEI | ULTEM™ |