Tenac™ 2013A
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Asahi Kasei Corporation |
| Trademark: | Tenac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZfV49R_Tenac2013A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™2013A is a polyoxymethylene (POM) homopolymer product,. It is available in North America, Africa and the Middle East, Europe or Asia Pacific. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.7 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.8 - 2.2 | % | Internal method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 94 | ASTM D785 | |
| Class r | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 68.0 | MPa | ISO 527-2 |
| -- | 65.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture | 55 | % | ASTM D638 |
| Fracture | 50 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2600 | MPa | ASTM D790 |
| -- | 2500 | MPa | ISO 178 |
| Flexural Strength | 92.0 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 13.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179 |
| Notched Izod Impact | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 172 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 163 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 136 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 97.0 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 - 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+15 - 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Arc Resistance | 250 | sec | ASTM D495 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ B800 H grey VN4155CF UV | PolyOne Corporation | Nylon 6 | Bergamid™ |
| BMC A50 (MS) | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Celstran® PA66-GF50-02 P11 | Celanese Corporation | Nylon 66 | Celstran® |
| Geon™ Advex™ L6105 natural | PolyOne Corporation | PVC, Rigid | Geon™ Advex™ |
| LNP™ THERMOTUF™ RF002I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |