Order Products : sales@su-jiao.com
SCHULAMID® 6 GF 7 FR 4 K1681
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZfQHzb_SCHULAMID-6-GF-7-FR-4-K1681.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 7% glass fibre reinforced flame retardant PA-6 grade; incandescent wire test without flame; without PBDE; GWIT > 800°C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.4 | % | ISO 527-2/1A/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 3.5 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 35 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 208 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 170 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 218 | °C | ISO 306/A120 |
| -- | 205 | °C | ISO 306/B50 |
| Ball Pressure Test (200°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.380 mm | V-2 | ||
| 1.50 mm | V-2 | ||
| 3.00 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.380 mm | 850 | °C | |
| 0.750 mm | 850 | °C | |
| 1.50 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.380 mm | 825 | °C | |
| 0.750 mm | 825 | °C | |
| 1.50 mm | 850 | °C | |
| Oxygen Index | 23 | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1385 UP | RTP Company | PPS | RTP |
| Geon™ Vinyl Flexible XV3887 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LNP™ LUBRICOMP™ DFL32P compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| TAFMER™ H-1030S | Mitsui Chemicals, Inc. | PAO | TAFMER™ |
| LNP™ LUBRICOMP™ EFL36 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |